PENGARUH SHOT PEENING TERHADAP STREES CORROSION CRACKING BAJA KARBON RENDAH YANG TELAH DI MILLING DAN TEMPERING DALAM LINGKUNGAN AIR LAUT

Mohammad , Badaruddin (2006) PENGARUH SHOT PEENING TERHADAP STREES CORROSION CRACKING BAJA KARBON RENDAH YANG TELAH DI MILLING DAN TEMPERING DALAM LINGKUNGAN AIR LAUT. POROS, 9 (4). pp. 264-268. ISSN 1410-6841

[img]
Preview
PDF (Jurnal) - Accepted Version
Download (1428Kb) | Preview

    Abstract

    This paper describes the effect of shot peening for stress corrosion cracking in a low carbon steel in sea water environment. The dimension of specimens test for tensile test and corrosion test were provided in according to JIS 2201 and ASTM G39, respectively. The corrosion cracking test was carried out by immersing into ocean water environment,(ASTM D1141). A test results showed that the shot peening process can improve the mechanical properties of the material significantly after the milling process. Whereas from the corrosion test the pitting corrosion is dominantly nucleated at the metal film interface. The specimens of shot peened do not show the significantly effect on attack both the pitting corrosion and the uniform corrosion. The biggest pitting corrosion was occurred under the static loading of 70% for the specimens unpeened. The presence of pitting corrosion promotes stress corrosion cracking. The cracking has the intergranular branched morphology which is typical for chloride cracking of a low carbon steel

    Item Type: Article
    Uncontrolled Keywords: shot peening, pitting corrosion, intergranular cracking, low carbon steel
    Subjects: T Technology > TJ Mechanical engineering and machinery
    T Technology > TN Mining engineering. Metallurgy
    Divisions: Fakultas Teknik > S1 Teknik Mesin
    Depositing User: Fakultas Teknik Mesin
    Date Deposited: 14 May 2013 11:16
    Last Modified: 14 May 2013 11:16
    URI: http://repository.unila.ac.id/id/eprint/189

    Actions (login required)

    View Item